<![CDATA[SoliForum - 3D Printing Community — Taulman t-glase]]> 2014-11-07T04:38:16Z PunBB https://www.soliforum.com/topic/3722/taulman-tglase/ <![CDATA[Re: Taulman t-glase]]> I received some T glass today. So far it is doing ok, not perfect but ok. Extruder at  215 and bed at 80. I am tryng to print this now  http://www.thingiverse.com/thing:510270 I know that T glass is  FDA appoved. Even the mesh is manifold , with ABS it sprung a leak. I found some food grade silicon that I thought might be usable to coat the outside to plug any holes
Just about ready to test the latest T glass print for leaks , pics to follow.

]]> https://www.soliforum.com/user/574/ 2014-11-07T04:38:16Z https://www.soliforum.com/post/71030/#p71030 <![CDATA[Re: Taulman t-glase]]> Why not just throw the .stl into something like Blender and use a solidify modifier? It's literally 6 clicks after opening.

]]> https://www.soliforum.com/user/3013/ 2014-09-03T08:17:19Z https://www.soliforum.com/post/65241/#p65241 <![CDATA[Re: Taulman t-glase]]> I finally got my TGlase working. Kind of.

First of all, it sticks best to glass. Once I swapped back to glass from buildtak I had no sticking issues.

The best word for it seems to be "stringy". It is more difficult to get good accurate prints than ABS or PLA. However it is definitely stronger and stiffer than ABS.

I printed a small bottle and amazingly the screw on cap worked. However the design was flawed. The walls were too thin and the bottle split in multiple places. I WOULD reinforce it with my CAD software BUT NO, that guy just had to hop on the Thingiverse bandwagon and ONLY POST STLS, SO I CAN DO NOTHING!
(Sorry. I really hate only getting STLs.)

It is good for making anything that comes in contact with food since it is FDA Approved.

EDIT: 225C is a good temp.

]]> https://www.soliforum.com/user/1669/ 2014-08-30T20:16:30Z https://www.soliforum.com/post/64948/#p64948 <![CDATA[Re: Taulman t-glase]]> AZERATE wrote:

Thank you for the tip!
I think the light in the room coupled with a lees than perfect iphone image makes it look far worse than what it looks like in person.

Once I get my Rumba up and running I will take another stab it it shortly after running ABS tests.

Yep, get that Rumba working!

]]> https://www.soliforum.com/user/2291/ 2014-08-21T23:58:19Z https://www.soliforum.com/post/64074/#p64074 <![CDATA[Re: Taulman t-glase]]> Thank you for the tip!
I think the light in the room coupled with a lees than perfect iphone image makes it look far worse than what it looks like in person.

Once I get my Rumba up and running I will take another stab it it shortly after running ABS tests.

]]> https://www.soliforum.com/user/4188/ 2014-08-21T23:50:21Z https://www.soliforum.com/post/64073/#p64073 <![CDATA[Re: Taulman t-glase]]> try increasing your layer height.

with the .6 nozzle I was doing .4mm no prob.  It will help with giving it the "glass" look.

]]> https://www.soliforum.com/user/55/ 2014-08-21T23:16:13Z https://www.soliforum.com/post/64069/#p64069 <![CDATA[Re: Taulman t-glase]]> http://i.imgur.com/vPgvuMl.jpg

Sorry for the shaky iphone pic.
.2mm at 220E/60B with a .6mm nozzle.
Worked great with my existing PLA settings without a fan at stock speeds. Cool stuff.

Thanks to Stevos758 for coming off his stash wink

]]> https://www.soliforum.com/user/4188/ 2014-08-19T19:26:12Z https://www.soliforum.com/post/63780/#p63780 <![CDATA[Re: Taulman t-glase]]> Yesterday I dusted off my spool of t-glase and went into calibration mode for an upcoming project that will be printed in PET.

I am running a .6mm nozzle @ 220C with very impressive results. Had to tweak my destring settings slightly to account for the bigger nozzle. Watertight single walls no problem with no warping.  I forgot how good this stuff was.

]]> https://www.soliforum.com/user/55/ 2014-08-15T17:39:01Z https://www.soliforum.com/post/63424/#p63424 <![CDATA[Re: Taulman t-glase]]> You are most welcome and good luck!
I'm going to sleep

]]> https://www.soliforum.com/user/2291/ 2014-08-07T03:48:49Z https://www.soliforum.com/post/62434/#p62434 <![CDATA[Re: Taulman t-glase]]> Thanks comrade big_smile
Sometimes I just need to bounce my mind goop off others to confirm my insanity, or in the rare case, sanity. tongue

]]> https://www.soliforum.com/user/3013/ 2014-08-07T03:43:44Z https://www.soliforum.com/post/62431/#p62431 <![CDATA[Re: Taulman t-glase]]> I'm on my phone so searching is hard but we did some trials with pics.  Myself, Ldymox and someone else.  Got much better results the faster we went.  Ask her she'll remember.

]]> https://www.soliforum.com/user/2291/ 2014-08-07T03:40:19Z https://www.soliforum.com/post/62429/#p62429 <![CDATA[Re: Taulman t-glase]]> Huh, I just ran a 6min single .5mm walled box at 50mm/s at 240 degrees.
It came out pretty well, surprisingly.

I was having some problems last night where the filament would just moosh out of the Bulldogs side under the bearing.
So I figured I'd have to kill the speed, evidently not however.

]]> https://www.soliforum.com/user/3013/ 2014-08-07T03:36:19Z https://www.soliforum.com/post/62427/#p62427 <![CDATA[Re: Taulman t-glase]]> Bondo is fun just double the hardener it'll cure real fast.

]]> https://www.soliforum.com/user/2291/ 2014-08-07T03:31:37Z https://www.soliforum.com/post/62426/#p62426 <![CDATA[Re: Taulman t-glase]]> That stuff isn't real fond of moisture either.  What kind of problems are you having?  Is this with the Bulldog?

]]> https://www.soliforum.com/user/2291/ 2014-08-07T03:29:49Z https://www.soliforum.com/post/62425/#p62425 <![CDATA[Re: Taulman t-glase]]> My bad 212 is what I have that profile set to run at.

]]> https://www.soliforum.com/user/2291/ 2014-08-07T03:28:31Z https://www.soliforum.com/post/62424/#p62424